ISOTHANE 3000 series resins are polyether based thermoplastic polyurethane. They exhibit excellent mechanical properties, hydrolytic resistance, fungus resistance, and low temperature performance properties. ISOTHANE 3000 series can be processed by extrusion and injection molding.

ISOTHANE TPU resins are supplied in pellet form packed in 25kg moisture proof bags. All TPU resins have been dried before packing. ISOTHANE TPU resins should be stored in cool and dry environment in their original containers until be used. Storage temperature should not exceed 30°C. If only a portion of TPU resins was used from a bag, the remainder of TPU resins should be tightly closed.

TPU resins are hygroscopic and pre-drying of TPU resins is always a necessary step before processing. Depend on the climate, the granule exposed to the atmosphere will absorb moisture very quickly. The moisture might bring about partial degradation of polymers and the formation of bubbles or streaks in the molded and extruded parts. In order to ensure the efficient and successful processing into quality parts, the moisture content in TPU resins is recommended less than 0.02%.

Barrel and Motor

• High torque drive capacity at low speed
• Vented or standard barrels acceptable

• Compression ratios between 2:1 and 3:1
• Minimum L/D of 30/1

• Vertical and tangential
• Water cooling is recommended

• Streamlined breaker plates with screen packing is recommended
• Typical 40/80/80/40 mesh screens

• Streamline with good temperature control
• Land Length is generally 10 to 15 times the part thickness
• Coat-hanger manifold-type dies are recommended for extruding film and sheet
• Crosshead dies are recommended for wire, cable and hose jacketing
• Side-fed rotating dies are recommended for blown film

Barrel and Motor

• High torque drive capacity at low speed
• Vented or standard barrels acceptable

• Compression ratios between 2:1 and 3:1
• Metering screw with gradual transition zone

• Typical 6,000 to 15,000 psi
• Hold pressure 60 – 70% of forward time

• Slow to moderate
• Depends on gating, wall section and flow length

About the recommended injection molding temperatures, please view ISOTHANE individual data sheets.

Various additives can be used to enhanced the properties of ISOTHANE TPU resins, e.g. anti-blocking agents, antioxidant, UV stabilizers or release agents. Most additives supplied as master batches are available. But not all additives are compatible with ISOTHANE TPU resins. It is recommended to inquire of your suppliers or our technical service before compounding.

For ISOTHANE TPU resins, up to 20% of regrind may be recycled with virgin material depending on finished parts requirements. The regrind material has to be kept free of contamination, diced and dried before re-using. The material which has been contaminated, discolored or degraded is not suitable for recycling. TPU resins may decrease desired properties, e.g. hardness and mechanical properties, due to improperly mixing with regrind.

Before working with these products, it is essential that all operators are aware of the healthy and safety precautions. ISOTHANE TPU resins can be processed or machined over a wide range of temperature. There can be some smoke formation during processing. The smoke that contains some decomposition substances of TPU or additives may cause irritation to human body. Generally, the temperature does not exceed 240°C that can reduce decomposition formation. An effective extraction system, especially in the melt outlet zone, is necessary. The detail information concerning healthy and safety can be available in safety data sheets (SDS) or contact our technical service.