TPU树脂 - Polycaprolactone 耐水解酯类

项目名称

聚酯型 TPU 树脂 通用级

产品特性

ISOTHANE 2000 系列属於 Polycaprolactone 聚己内酯型 TPU 树脂，它们具备有优异之韧度丶机械强度丶耐磨耗性丶耐溶剂性以及耐水解性，适用於射出丶吹膜以及押出等用途。

应用场合

垫片丶轴衬丶胶皮丶薄膜丶管件丶电线电缆丶运动鞋底丶运动器材以及机械零件等。

项目名称

聚酯型 TPU 树脂 通用级

Description

ISOTHANE 2000 series products are poly(caprolactone) ester based thermoplastic polyurethane. They exhibit excellent mechanical properties, hydrolysis resistant, oil resistance and outstanding low compression set. These products can be injection molded and extruded.

Supply and Storage

ISOTHANE TPU resins are supplied in pellet form packed in 25kg moisture proof bags. All TPU resins have been dried before packing. ISOTHANE TPU resins should be stored in cool and dry environment in their original containers until be used. Storage temperature should not exceed 30°C. If only a portion of TPU resins was used from a bag, the remainder of TPU resins should be tightly closed.

Drying

TPU resins are hygroscopic and pre-drying of TPU resins is always a necessary step before processing. Depend on the climate, the granule exposed to the atmosphere will absorb moisture very quickly. The moisture might bring about partial degradation of polymers and the formation of bubbles or streaks in the molded and extruded parts. In order to ensure the efficient and successful processing into quality parts, the moisture content in TPU resins is recommended less than 0.02%.

A desiccant-bed-type hopper dryer is recommended for drying ISOTHANE TPU. The dew point of the inlet air should be in the range of -30 to -40°C. About the recommended drying conditions, please view ISOTHANE individual data sheets.

Processing - Extrusion

Barrel and Motor

l   High torque drive capacity at low speed

l   Vented or standard barrels acceptable

Screw

l   Compression ratios between 2:1 and 3:1

l   Minimum L/D of 30/1

Feed Throat

l   Vertical and tangential

l   Water cooling is recommended

Screen Pack

l   Streamlined breaker plates with screen packing is recommended

l   Typical 40/80/80/40 mesh screens

Die

l   Streamline with good temperature control

l   Land Length is generally 10 to 15 times the part thickness

l   Coat-hanger manifold-type dies are recommended for extruding film and sheet

l   Crosshead dies are recommended for wire, cable and hose jacketing

l   Side-fed rotating dies are recommended for blown film

About the recommended extrusion temperatures, please view ISOTHANE individual data sheets.

Processing - Injection Molding

Barrel and Motor

l   High torque drive capacity at low speed

l   Vented or standard barrels acceptable

Screw

l   Compression ratios between 2:1 and 3:1

l   Metering screw with gradual transition zone

Injection Pressure

l   Typical 6,000 to 15,000 psi

l   Hold pressure 60 – 70% of forward time

Injection speed

l   Slow to moderate

l   Depends on gating, wall section and flow length

About the recommended injection molding temperatures, please view ISOTHANE individual data sheets.

Coloring

Generally, ISOTHANE TPU resins are supplied in their natural color. They can be colored by blending with pigment or pigment master batch. Using master batch based on TPU is recommended. Other master batch based on polyethylene or polystyrene is suitable to a limited extent. All colorants employed in TPU resins must be pre-dried before processing.

The normal addition of pigment or pigment master batch is 0.2%-0.5% or 1-3%.

Additives

Various additives can be used to enhanced the properties of ISOTHANE TPU resins, e.g. anti-blocking agents, antioxidant, UV stabilizers or release agents. Most additives supplied as master batches are available. But not all additives are compatible with ISOTHANE TPU resins. It is recommended to inquire of your suppliers or our technical service before compounding.

Recycling

For ISOTHANE TPU resins, up to 20% of regrind may be recycled with virgin material depending on finished parts requirements. The regrind material has to be kept free of contamination, diced and dried before re-using. The material which has been contaminated, discolored or degraded is not suitable for recycling. TPU resins may decrease desired properties, e.g. hardness and mechanical properties, due to improperly mixing with regrind.
Regulatory or testing organizations (e.g., UL) may have specific requirements limiting the allowance amount of regrind. Certain quality requirements laid down in specifications may exclude the use of regrind material.

Healthy and Safety Information

Before working with these products, it is essential that all operators are aware of the healthy and safety precautions. ISOTHANE TPU resins can be processed or machined over a wide range of temperature. There can be some smoke formation during processing. The smoke that contains some decomposition substances of TPU or additives may cause irritation to human body. Generally, the temperature does not exceed 240°C that can reduce decomposition formation. An effective extraction system, especially in the melt outlet zone, is necessary. The detail information concerning healthy and safety can be available in safety data sheets (SDS) or contact our technical service.

Disposal

ISOTHANE TPU resins present no hazard to the environment or water. They can be dumped on municipal landfill or in a waste incineration plant. The official regulations on waste disposal should be observed.

项目

Units

ASTM

2090A-M

2095A-M1

2090A-MH

2095A-MH

2050D-MH

比重

D-792

1.20

1.20

1.20

1.20

1.20

硬度

Shore A
D

D-2240

91A

94A

90A

95A

51D

抗拉强度

MPa
psi

D-412

56
8,180

56
8,060

30
4,400

33
4,780

34
4,980

抗拉模数 @ 50% 延伸率

MPa
psi

D-412

9
1,310

12
1,690

6
910

14
2,020

18
2,630

抗拉模数 @ 100% 延伸率

MPa
psi

11
1,620

15
2,100

8
1,200

16
2,320

20
2,900

抗拉模数 @ 300% 延伸率

MPa
psi

26
3,700

35
5,130

14
2,050

24
3,510

26
3,770

断裂延伸率

%

D-412

450

390

580

460

440

压缩变形率
22 hrs @ 23°C
22 hrs @ 70°C
22 hrs @ 100°C
70 hrs @ 100°C

%

D-395
(B)

20
28
-
-

20
29
-
-

-
-
33
45

-
-
30
38

-
-
30
38

撕裂强度

N/mm
lb/in

D-624
DIE C

120
680

164
900

130
760

180
1,050

180
1,040