比重:1.82~1.84

Testing Item ASTM Unit Value
Tensile strength
Tensile elongation
D-638
D-638
Kg/cm2
%
400 ↑
2.0 ↑
Flexural strength
Flexural modulus
D-790 Kg/cm2
Kg/cm2
700 ↑
70000 ↑
Izod impact
(1/8", V-notched)
D-256 Kg ‧ cm/cm
( 23°C )
( -30°C )
10.0 ↑
-
Heat distortion temperature D-648 °C
(4.6 Kg/cm 2)
(18.6 Kg/cm 2)
-
-
Melt index D-1238 g/10min
(235°C / 2.16kg)
(275°C / 2.16kg)
-
-
Hardness D-785
D-785
D-2240
Rockwell R
Shore A
Shore D
-
-
-
Mold shrinkage D-955 flow direction %
perpendicular direction %
-
-
Specific gravity D-792 - 1.82~1.84
Ash content D-482 % -
Flammability UL-94 (1/16")
(1/32")
-
-

High specific gravity blends,PLA base.(1.82~1.84)
Pretreatment:23℃‚50% RH‚24hrs

 

应用说明:BB弹、化妆品外壳、筹码